Electrotyping (also galvanoplasty) is a chemical method for forming metal parts that exactly reproduce a model. The method was invented by Moritz von Jacobi in Russia in 1838, and was immediately adopted for applications in printing and several other fields.1 As described in an 1890 treatise, electrotyping produces "an exact facsimile of any object having an irregular surface, whether it be an engraved steel- or copper-plate, a wood-cut, or a form of set-up type, to be used for printing; or a medal, medallion, statue, bust, or even a natural object, for art purposes."2 In art, several important "bronze" sculptures created in the 19th century are actually electrotyped copper, and not bronze at all;3 sculptures were executed using electrotyping at least into the 1930s.4 In printing, electrotyping had become a standard method for producing plates for letterpress printing by the late 1800s. It complemented the older technology of stereotyping, which involved metal casting.5 By 1901, stereotypers and electrotypers in several countries had formed labor unions around these crafts.678 The unions persisted into the 1970s, but by the late 20th century, after more than a century in widespread use for preparing plates, the two technologies had been bypassed by the transitions to offset printing and to new techniques for the preparation of printing plates.910
As with metal casting and stereotyping, a mold is first formed from the model. Since electrotyping involves wet chemical processes and is done near room temperature, the molding material can be soft. Materials such as wax, gutta-percha (natural latex), and ultimately ozokerite were used. The mold's surface is made electrically conducting by coating it very thinly with fine graphite powder or paint. A wire is attached to the conducting surface, and the mold is suspended in an electrolyte solution.5
Electrotyping is activated by electrical currents that flow between anode wires that are also immersed in the solution and the wire connected to the coated mold (the cathode). For copper electrotyping, a typical aqueous electrolyte contains copper sulfate (CuSO4) and sulfuric acid (H2SO4), and the anode is also copper; the arrangement is illustrated in the figure. The electrical current causes copper atoms to dissolve from the anode's surface and to enter the electrolyte as copper ions (Cu++ in the figure). Copper ions are taken up by the mold's conducting surface at the same rate at which copper dissolves from the anode, thus completing the electrical circuit.11 When the copper layer on the mold grows to the desired thickness, the electrical current is stopped. The mold and its attached electrotype are removed from the solution, and the electrotype and the mold are separated.5 An animation of the electrotyping process was produced in 2011 by the Metropolitan Museum of Art.12 Other metals besides copper can be electrotyped; similar procedures apply, but each different metal needs its own anode and electrolyte chemicals.
There is a second type of electrotyping that has been used in which the copper film is deposited onto the outside of a form, and is not separated from it. In this use the form is typically waterproofed plaster, which remains as a core after electrotyping. In German this method is known as Kerngalvanoplastik; the more usual technique described in the previous paragraph is known as Hohlgalvanoplastik.4
Electrotyping is related to electroplating, which permanently adds a thin metallic overlayer to a metallic object instead of creating a freestanding metal part.13 Electrotyping and electroforming both produce metal parts, but differ in technical details. Electroforming involves the production of a metallic part around a metallic mandrel, although the term is sometimes used more broadly to encompass all electrodeposition processes.14 As noted above, electrotyping forms the part using a non-conducting mold or form whose surface has been made conducting by applying a thin coating or graphite or metal powder.
At present, most sources credit Moritz Hermann Jacobi with the invention of "galvanoplasty" or electrotyping in 1838; Jacobi was a Prussian scientist who was working in St. Petersburg, Russia.14 19th century accounts often credited Thomas Spencer or C. J. Jordan with the invention in England, or Joseph Alexander Adams in the United States; Heinrich in particular gave a thorough account of the controversies surrounding the crediting of the invention, along with a short biography of Jacobi, in an article honoring the centennial of electrotyping in 1938.1
The electrotyping industry was limited for some decades by the sources of the electrical currents needed to activate the deposition of metal films into the mold; the rate of film growth is proportional to the magnitude of this current. In the initial work, the Daniell cell was used to provide these currents. The Daniell cell was largely replaced by the Smee cell (amalgamated zinc and platinized silver in sulfuric acid) after the latter's invention by Alfred Smee in 1840.15 Both of these cells are forerunners of contemporary electrical batteries. By the 1870s, mechanical generators were being used; the larger currents that could be sustained by generators enabled substantial increases in the rate of metal deposition during electrotyping.5
One of the first applications of electrotyping was in printing. Initially, electrotyping was used to make copper reproductions of engraved metal plates or wooden carvings, which were used to print artwork. The electrotypes could be incorporated along with movable type to compose the formes for printing. Jacobi published his first account of electrotyping in October, 1838. In 1839, electrotyping was used by Russian printers for government documents; the Russian Czar Nicholas I had immediately become an enthusiastic supporter and patron of the technology. In England, the first use of electrotyping for printing appeared in the London Journal of April 1840, and other English examples are known from later in that year. The image to the right shows one of the earliest uses of electrotyping in the United States; it is a comparison done by Joseph Alexander Adams in 1841 of the printed image prepared directly from a wood carving and of the image printed from a copper electrotype copy. Electrotyped copper plates could be formed into cylinders, which was valuable for use in magazine and newspaper printing.1
Electrotyping was also used to produce entire printing plates directly from the formes composed from movable type and illustrations. In this application, electrotyping was a higher quality but more costly alternative to stereotyping, which involved casting of type metal into a mold prepared from the forme. Stereotyping had been invented around 1725, and was already well-established when electrotyping was invented in 1838. Both methods yielded plates that could be preserved in case of future needs, for example in the printing of novels and other books of unpredictable popularity. The movable type used to compose the original forme could then be re-used. Both methods could be used to prepared curved plates for rotary presses, which were used for the longest print runs. The widespread adoption of electrotyping for this use occurred after mechanical electrical generators (dynamos) became commonly available around 1872. These generators supplanted the whole rooms of chemical batteries (Smee cells) that were previously used to provide electricity for electrotyping. Batteries did not have the electrical capacity needed to rapidly deposit the electrotype (or "electro"). The advent of plating dynamos sped up electrotyping twenty times or more, so that an electrotype printing plate could be deposited in less than two hours. In addition, the chemical batteries gave off toxic fumes that had required their isolation in separate rooms.5
By the 1900s printing plants often incorporated electrotyping and stereotyping departments, and electrotyping and stereotyping had become trades with associated apprenticeships.5 In the United Kingdom, the National Society of Electrotypers and Stereotypers (NSES) formed in 1893, and continued to 1967 when it amalgamated with the National Graphic Association.6 In the US and Canada, the International Stereotypers and Electrotypers Union (ISEU) was formed in 1902; previously, electrotypers had belonged to the International Typographer's Union (ITU). In 1925 there were 6800 members, and in 1955 10,500.816 In 1973 the ISEU was absorbed into the International Printing and Graphic Communications Union.7 In 1978, an Occupational Outlook Handbook reported that 2000 electrotypers and stereotypers were employed in the US. However, job prospects were reported as poor.9 Offset printing has supplanted letterpress printing in most printing plants; the last letterpress facility for a newspaper was installed in the 1980s. For offset printing, the printing plates are typically prepared by coating them with light-sensitive materials, and creating the image on the plate by direct optical exposure (the photo-offset process); stereotyping and electrotyping are not used.10
Electrotyping has been used for the production of metal sculptures, where it is an alternative to the casting of molten metal. These sculptures are sometimes called "galvanoplastic bronzes", although the actual metal is usually copper. It was possible to apply essentially any patina to these sculptures; gilding was also readily accomplished in the same facilities as electrotyping by using electroplating. Electrotyping has been used to reproduce valuable objects such as ancient coins, and in some cases electrotype copies have proven more durable than fragile originals.
One of the earliest documented large-scale (1.67 metres (5.5 ft)) electrotype sculptures was John Evan Thomas's Death of Tewdric Mawr, King of Gwent (1849). The electrotype was done by Elkington, Mason, & Co. for the Great Exhibition of 1851.17 Among the most spectacular early examples are Josef Hermann's twelve angels (1858) at the base of the cupola of Saint Isaac's Cathedral in St. Petersburg, Russia (see photograph A below). As described by Théophile Gautier in 1867, "They are twenty-one feet high, and were made by the galvanoplastic process in four pieces, whose welding together is invisible. They could in this manner be made so light that, in spite of their dimensions, they would not be too heavy for the cupola. This crown of gilt angels, poised amid a flood of light, and shining with rich reflections, produces an extremely rich effect."18 Other important sculptures followed; David A. Scott has written, "Some extremely important commissions were made in electrotypes, such as the "bronzes" that adorn the Opera, Paris, and the 320 cm high statue of Prince Albert and four accompanying figures, erected behind the Albert Hall in London as a memorial to the Great Exhibition of 1851."3 The statue of Prince Albert was unveiled in 1861 (see photograph B below); the electrotyping process "was one in which the Prince Consort had had great faith."19 The Palais Garnier in Paris (the Opera) has two 7.5 meter tall sculptures above the main facade; the building was completed in 1869 (see photograph C below).
In the 19th century, museums often displayed electrotypes of ancient coins instead of the originals (see photograph D below), and individuals purchased electrotypes for their private collections.2021 By 1920, the Victoria and Albert Museum in England had acquired nearly 1000 electrotyped copies of important objects from the collections of other European museums. The most celebrated may be their copy of the Jerningham wine cooler, which is a spectacular silverwork made in England in 1735 that has long been in the collection of the Hermitage Museum in Russia.22 Many of these objects were made by Elkington & Co., which had an extensive business in electrotyped silver.
An important example of electrotyping's use for preservation is the electrotype of the plaster life-mask of the poet John Keats (see photograph E below). The original life mask was made by Haydon in 1816. The plaster mask was electrotyped in 1884 by Elkington & Co., and this copper copy is now apparently in better condition than the plaster original.23
From 1890 through at least 1930, the Abteilung für Galvanoplastic of the WMF Company in Germany produced many statues and other items using electrotyping. The statues in particular were significantly less expensive than bronze castings.24 Memorials in German cemeteries from this era often incorporated electroptyped statues from models that had been commissioned by WMF from well-known sculptors (see photograph F below).4 WMF also undertook larger commissions.4 One example is the full-sized copper electrotype (1911) of Ernst Rietschel's 1857 bronze for the Goethe–Schiller Monument in Weimar, Germany, which is about 3.5 metres (11 ft) tall (see photograph at right).
Many sculptors have experimented with the technique of electrotyping a plaster form that remains as the core of the finished sculpture (Kerngalvanoplastik). As one example, the sculptor Elie Nadelman did several significant sculptures in the 1920s and 1930s using this technique.25 The advantage was that Nadelman could have these "galvanoplastique" metal sculptures made quickly and inexpensively. Such sculptures can degrade quickly, and have presented significant preservation and restoration problems.26
A. Among the earliest and most spectacular large sculptures produced by copper electrotyping were twelve gilt angels (ca. 1858) by Josef Hermann that stand in the cupola of Saint Isaac's Cathedral in St. Petersburg, Russia. These sculptures are 6 metres (20 ft) tall; the metal needed to be thin enough so that the weight of the sculptures could be supported high above the cathedral's floor.18
D. Electrotypes of 5th century coins from the Canterbury-St Martin's hoard in England. Electrotype copies of coins and antiquities were produced for museum display and for private collectors.
- Heinrich, Herbert (December 1938). "The Discovery of Galvanoplasty and Electrotyping". Journal of Chemical Education: 566–575. Electrotyping was immediately recognized as an important industrial process, and several individuals claimed to have invented it around 1838. Heinrich reviewed this history on the occasion of the centennial of its invention, and concludes that Jacobi was indeed the inventor of "galvanoplasty" or electrotyping.
- McMillan, Walter George (1890). "VIII. Electrotyping". A treatise on electro-metallurgy. London: C. Griffin and company. McMillan wrote particularly clearly, and was the author of the 1911 Encyclopædia Britannica entry on electrotyping.
- Scott, David A. (2002). Copper and bronze in art: corrosion, colorants, conservation. Getty Publications. ISBN 978-0-89236-638-5. "Some extremely important commissions were made in electrotypes, such as the "bronzes" that adorn the Opera, Paris, and the 320 cm high statue of Prince Albert and four accompanying figures, erected behind the Albert Hall in London as a memorial to the Great Exhibition of 1851. The Prince Albert statue was electrotyped by Elkington & Company of Birmingham, England, in 1861 and has recently been restored." The Memorial to the Great Exhibition was originally erected in the garden of the Royal Horticultural Society, and moved to its present location around 1890.
- Meißner, Birgit; Doktor, Anke (2000). "Galvanoplastik – Geschichte einer Technik aus dem 19. Jahrhundert" [Galvanoplastik - History of a Technology from the 19th Century]. In Meißner, Birgit; Doktor, Anke; Mach, Martin. Bronze- und Galvanoplastik: Geschichte – Materialanalyse – Restaurierung (in German). Landesamt für Denkmalpflege Sachsen. pp. 127–137.
- Hatch, Harris B.; Stewart, Alexander A. (1918). "History of Electrotype Making". Electrotyping and stereotyping. Chicago: United Typothetae of America. p. 4. "Perhaps one of the greatest forward steps in connection with electrotyping was made when the plating dynamo was invented. The first adoption of a dynamo, in place of the Smee type of battery, was by Leslie, of New York, in 1872." Primer for apprentices in the printing industry. Good short introduction to the history of electrotyping.
- "The Print unions". Unite - the Union. Retrieved 2011-11-09.
- The International Stereotypers and Electrotypers Journal was published from 1906 through 1973. See "Walter P. Reuther Library International Stereotypers and Electrotypers Journal". Retrieved 2011-11-04.
- Cunningham, Ed; Reed, Leonard (1955). Guide to earning a living: a complete survey of careers in business, the professions, trade, agriculture, and government service. Simon and Schuster. p. 102.
- US Bureau of Labor Statistics (1980). Occupational Outlook Handbook. p. 46.
- Kipphan, Helmut, ed. (2001). "Printing Technologies with Permanent Printing Master". Handbook of Print Media: Technologies and Production Methods. Springer. ISBN 354067326 Check
- The electrochemical transfer of copper from a copper electrode through an electrolyte to the cathode is treated in contemporary textbooks as an example of an "active electrode" and also of electrorefining. One reference with some online availability: Fernandes, Raymond. Chemistry 10. Ratna Sagar. p. 85. ISBN 978-81-8332-379-6. Retrieved 2011-12-06.. A second reference is: Oxtoby, David W.; Nachtrieb, Norman H.; Freeman, Wade A. (1990). Chemistry: Science of Change. Saunders College Publishing. pp. 521–523. ISBN 0-03-004814-1.
- Alcorn, Ellenor (2011). "An Art of Attraction: The Electrotyping Process". Metropolitan Museum of Art & Dynamic Diagrams, Inc. Retrieved 2011-12-16. 3-D animation that explains the use of electrotyping to create presentation copies of works of art. The example is the electrotyping of the James Horton Whitehouse's Bryant Vase (1875) by Tiffany & Co.. The video was produced in conjunction with the exhibit Victorian Electrotypes: Old Treasures, New Technology (November 22, 2011 – April 22, 2012).
- Graf, Rudolph (1999). Modern Dictionary of Electronics. Newnes. p. 245. "electroplating. The deposition of an adherent metal coating on a conductive object for protection, decoration, or other purposes, such as securing a surface with properties or dimensions different from those of the base metal. The object to be plated is placed in an electrolyte and connected to one terminal of a dc voltage source. The metal to be deposited is similarly immersed and connected to the other terminal."
- Graf, Rudolph (1999). Modern Dictionary of Electronics. Newnes. p. 240. "electroforming. 3. The production or reproduction of articles by electrodeposition on a mandrel or mold that is subsequently separated from the deposit."
- Gordon, James Edward Henry (1880). A physical treatise on electricity and magnetism, Volume 1. D. Appleton and Company. p. 207.
- American Labor Year Book, 1926. pp. 85–87, 103–172.
- Simon, Jacob (February 2011). "British bronze sculpture founders and plaster figure makers, 1800-1980 - E". National Portrait Gallery.
- Gautier, Théophile; Tyson, Florence MacIntyre (1905). Russia, Volume 1. The J.C. Winston Co. p. 316. "Twelve great gilt angels, taking the part of the caryatides, support consoles on which stand the bases of the pilasters which form the interior row of the dome and separate the windows. They are twenty-one feet high, and were made by the galvanoplastic process in four pieces, whose welding together is invisible. They could in this manner be made so light that, in spite of their dimensions, they would not be too heavy for the cupola. This crown of gilt angels, poised amid a flood of light, and shining with rich reflections, produces an extremely rich effect." This book incorporates a translation of Gautier, Théophile (1866). Voyage en Russie Voyage in Russia (in French). Charpentier. The angels were sculpted by Josef Hermann; see Rice, Christopher (2010). DK Eyewitness Travel Guide: St. Petersburg. Penguin. ISBN 978-0-7566-6493-0..
- Sheppard, F. H. W., ed. (1975). "The Memorial to the Exhibition of 1851". Survey of London. Volume 38: South Kensington Museums Area. Institute of Historical Research. Retrieved 2011-11-07.
- Dept. of Coins and Metals. Barclay Vincent, Head. (1898). A guide to the select Greek and Roman coins exhibited in electrotype. London: The British Museum.
- Jones, Mark (1990). Fake?: The Art of Deception. University of California. ISBN 978-0-520-07087-5. Electrotyping produces copies of objects that are not difficult to distinguish from originals, but this book contains a series of photographs illustrating the steps in making an electrotype of a gilded silver dish.
- "Covered urn". Victoria and Albert Museum. Retrieved 2011-11-05.
- Colvin, Sir Sidney (1917). John Keats: his life and poetry, his friends, critics and after-fame. C. Scribner's Sons. p. xi.
- Simon, Jacob (March 3, 2011). "Bronze sculpture founders: a short history". National Portrait Gallery. "Electrotypes generally cost some 25-30% less than traditionally cast work. Apart from this cost saving, it was argued that there were advantages to be had in the finishing process: ‘It is not necessary to relieve the surface of that general roughness which is always the result of ordinary metal castings, and which, when not effected by an artist, often destroys the beauty of the modelling.’ (‘Electro-metallurgy’, Art Journal, 1866, vol.5, pp.286-7). There were however adverse comments about the appearance of electrotypes which could seem rather bright until the surface gained a patina."
- Nadelman, Cynthia (2001). "Plastiques Fantastiques". Elie Nadelman: Galvano-Plastiques. Salander/O’Reilly Galleries. Exhibit catalog.
- "Elie Nadelman: The Cleaning and Conservation of Elie Nadelman’s Two Circus Women, 1930, January – April 2010". Retrieved 2011-12-12.
- Gjertson, Stephen (June 28, 2010). "The Paris Opéra: Charles Garnier’s Opulent Architectural Masterpiece". Stephen Gjertson Galleries. "Charles-Alphonse-Achille Gumery, Harmony, 1869. Gilded galvanoplastic bronze, height: 24' 7 1/4, west facade attic group."
- Easson, John (2004). "Stereotyping and Electrotyping". British Publishing Society. A3 format poster explaining these aspects of printing. This poster is part of a series of 34 by Easson; see History of Printing.
- Langbein, George; Brannt, William Theodore (1898). A complete treatise on the electro-deposition of metals. Third American Edition. Philadelphia: H.C. Baird & Co. Based on Langbein's Handbuch der Galvanischen Metall-Metallniederschläge. Langbein published six editions of this handbook in German, as well as cooperating with versions in English such as this one; see Georg Langbein (in German). This "American edition" has numerous figures illustrating technical procedures for electrodeposition.
- Partridge, C. S. (1908). Electrotyping: A Practical Treatise on the Art of Electrotyping by the Latest Known Methods (Second Edition). Chicago: The Inland Printer Company.
- Rice, Roy (1982). "Matrix Making at the Oxford University Press".
- Wahl, William Henry; Roseleur, Alfred (1883). Galvanoplastic manipulations: A practical guide for the gold and silver electroplater and the galvanoplastic operator. Philadelphia: H. C. Baird. Based on Manipulations Hydroplastique. Chapter LIX has a very complete description of the steps in electrotyping for printing, with figures.
- "About Electroformed Bronze". Retrieved 2011-12-11. Commercial website traces the history of one manufacturer of electrotyped art metal in the US from the 1880s through the 1930s. The firm was created by P. Mori and Sons, who manufactured objects with the brand name Galvano Bronze. Subsequent names included: Pompeian Bronze, Armor Bronze, Marion Bronze, Kathodion Bronze Works and LaFrance Bronze Arts.